Two Components Polyurea Waterproof Coating TH801

Descriptions

TH801 is a polyurea elastomer for construction waterproof, general   engineering

Typical uses

Factory building, ancient town, office block, community

Proportion &

Packaging

Component A: Component   B= 1:1

Component A: 220KG/bucket Component B: 210KG/bucket 

One 20' container loads 80 buckets/17.2 ton

Storage conditions

1. The storage   temperature should be 5-40ºC.
2. Under normal storage and transportation conditions, the storage period is not less than 6 months from the date of

production.
3. Store in a cool, ventilated environment, avoid direct sunlight, prohibit close to fire sources, and prevent collisions.

Construction   Notes 

1. During   construction, the temperature of the substrate must be 3°C higher than the   dew point temperature.
2. Before the product is used, component B should be fully stirred.
3. The system has a 100% solid content, and it is strictly forbidden to add   any diluent.
4. When constructing in a confined space, maintain good ventilation.
5. When using this product, you need to wear work clothes, goggles, gas   masks, gloves and other protective equipments. 

Features &

advantages

Extraordinary physical properties.

1. 100% solid, solvent-free construction safety and eco-friendly.

2. Fast cure, sprayed and formed on any curved surface without sagging.

3. Moisture and temperature insensitivity during processing.

4. High thermal stability. High resistance to freeze-thaw.

5. high adhesion. high elongation, high tear strength.

6. Seamless, flexible, waterproof and anti-corrosion.

7. No chalking and fading in long-term outdoor use.

Item

Technical Index

GB/T23446-2009 I

TH-801

Solid content (%)

≥96

99

Gel time(s)

≤45

15

Surface drying time (s)

≤120

35

Tensile strength (Mpa)

≥10

15

Elongation at   break(%)

≥300

380

Tear strength (N/mm)

≥40

66

Foldability at low   tempetature(℃)

≤-35

-40

Water   impermeability(0.4Mpa,2H)

No water leakage

No water leakage

Dimensional change   on heating

Extension(%)

≤1.0

0.5

Shrinkage(%)

≤1.0

0.5

Adhesion strength(Mpa)

≥2.0

2.5

Water absorption(%)

≤5

2.5

Aging properties at   maintained extension

Heat aging

No crack & deformation

No crack & deformation

Artificial aging

No crack & deformation

No crack & deformation

Heat aging

Retention of   tensile strength(%)

80～150

96

Elongation at   break(%)

≥250

350

Foldability at low   tempetature(℃)

≤-30

-32

Alkali treatment

Retention of   tensile strength(%)

80～150

100

Elongation at   break(%)

≥250

330

Foldability at low   tempetature(℃)

≤-30

-33

Acid treatment

Retention of   tensile strength(%)

80～150

95

Elongation at   break(%)

≥250

343

Foldability at low   tempetature (℃)

≤-30

-33

Salt treatment

Retention of   tensile strength(%)

80～150

95

Elongation at   break(%)

≥250

358

Foldability at low   tempetature (℃)

≤-30

-32

Artificial aging

Retention of   tensile strength(%)

80～150

93

Elongation at   break(%)

≥250

330

Foldability at low   tempetature (℃)

≤-30

-32

Hardness(Shore A)

≥70

90±5

Wear resistance(750g/500r)/mg

≤40

20

Impact resistance (kg/m)

≥0.6

1.0

Color

Customized